Analysis of the Influence of Plastic Parts Defects on Plating Surface

The bad performance of the rubber parts is: bruise/scratch. The effect after plating is: more obvious after plating, affecting the appearance.

The bad performance of the rubber parts is: batch peak. The effect after electroplating is that the electroplated layer is still deposited after electroplating, which is easy to cause scratching and affects assembly.

The bad performance of the rubber parts is: water line; gas pattern. The effect after electroplating is: it is still clearly visible after electroplating, because the electroplating itself is thin (2--30um), it is difficult to achieve by electroplating alone.

The bad performance of the rubber parts is: plastic bottles. The effect after plating is: it can't be covered after electroplating, which affects the appearance.

The bad performance of the rubber parts is: glue/plastic scraps. The effect after electroplating is: metal swarf after electroplating, which affects the assembly and easily damages the plating bath solution.

The bad performance of the rubber parts is: impurities. The effect after electroplating is: after plating, it will cause sand, blistering, and leakage plating, which will affect the appearance.

The bad performance of the rubber parts is: shrinkage holes. The effect after electroplating is: easy to hide the plating solution, affecting the composition of the plating bath liquid, resulting in leakage of the workpiece.

The bad performance of the rubber parts is: use of mold release agent. The effect after electroplating is: easy to cause leakage plating, and the plating component has poor bonding force and oil stain.

The bad performance of the rubber parts is: too much water. The effect after electroplating is: it is easy to cause pitting, and the plating parts are leak-plated, the adhesion is poor, and the nozzle material does not exceed 30% at most.

The bad performance of the rubber parts is: stamping / fire pattern / dragging. The effect after plating is: more obvious after plating, affecting the appearance.

Matte etching of electroplated parts: the surface etch thickness requirements are consistent, especially semi-gloss chrome products, the etched lines should be fine or no matte effect.

The composition of the electroplated parts: the electroplating grade ABS is the best, you can also use the ordinary ABS, the ingredients are applied with new materials, and no color powder can be added.

Packing method of electroplated parts: It is preferred to use a single box of blister box, a single set of PE bags, and a large piece of inner cotton, and a bubble bag.

The setting of the hanging position of the plated parts: no proper hanging position is easy to cause deformation, and the connection between the parts and the nozzle is not good, which will cause the current to be not good, causing yellowing and leakage plating.